[Datasheet Apec DP1-9354]

Developmental product, flame retardant: V-0/1,5mm (UL 94), V-0/3,0mm (UL 94), 5VA/3mm (UL 94), softening temperature (VST/B 120)=185 °C, only opaque colours available, Halogen lamp housings Insulator of busbars

Datasheet-Download

Property		Test Condition	Unit	Standard	Value
Rheological properties
	Melt volume-flow rate	330 °C; 2.16 kg	cm³/10 min	ISO 1133	11
	Melt mass-flow rate	330 °C; 2.16 kg	g/10 min	ISO 1133	11
Mechanical properties (23 °C/50 % r. h.)
	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	2400
	Yield stress	50 mm/min	MPa	ISO 527-1,-2	72
	Yield strain	50 mm/min	%	ISO 527-1,-2	6.8
	Nominal strain at break	50 mm/min	%	ISO 527-1,-2	50
	Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	N
	Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	N
	Flexural modulus	2 mm/min	MPa	ISO 178	2400
	Flexural strength	2 mm/min	MPa	ISO 178	105
	Ball indentation hardness		N/mm²	ISO 2039-1	120
Thermal properties
	Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	159
	Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	174
	Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	185
	Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.7
	Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.7
	Burning behavior UL 94 (1.5 mm) [UL recognition]	1.5 mm	Class	UL 94	V-0
	Burning behavior UL 94	3.0 mm	Class	UL 94	V-0
	Burning behavior UL 94-5V	3.0 mm	Class	UL 94	5VA
	Oxygen index	Method A	%	ISO 4589-2	35
	Glow wire test (GWFI)	1.0 mm	°C	IEC 60695-2-12	960
Electrical properties (23 °C/50 % r. h.)
	Relative permittivity	100 Hz	-	IEC 60250	3
	Relative permittivity	1 MHz	-	IEC 60250	3
	Dissipation factor	100 Hz	10-4	IEC 60250	7
	Dissipation factor	1 MHz	10-4	IEC 60250	80
	Volume resistivity		Ohm·m	IEC 60093	1E14
	Surface resistivity		Ohm	IEC 60093	4E15
	Electrical strength	1 mm	kV/mm	IEC 60243-1	30
	Comparative tracking index CTI	Solution A	Rating	IEC 60112	225
	Comparative tracking index CTI M	Solution B	Rating	IEC 60112	<100
	Electrolytic corrosion		Rating	IEC 60426	A1
Other properties (23 °C)
	Water absorption (saturation value)	Water at 23 °C	%	ISO 62	0.3
	Water absorption (equilibrium value)	23 °C; 50 % r. h.	%	ISO 62	0.12
	Density		kg/m³	ISO 1183-1	1150
Material specific properties
	Refractive index	Procedure A	-	ISO 489	-
	Luminous transmittance (clear transparent materials)	1 mm	%	ISO 13468-2	-
Processing conditions for test specimens
	Injection molding-Melt temperature		°C	ISO 294	330
	Injection molding-Mold temperature		°C	ISO 294	100
	Injection molding-Injection velocity		mm/s	ISO 294	200

Disclaimer

Disclaimer for Developmental products

* This is a developmental product. Further information, including amended or supplementary data on hazards associated with its use, may be compiled in the future. For this reason, no assurances are given as to type conformity, processability, long-term performance characteristics or other production or application parameters. Therefore, the purchaser/user uses the product entirely at his own risk without having been given any warranty or guarantee and agrees that the supplier shall not be liable for any damage, of whatever nature, arising out of such use.

Test values

Unless specified to the contrary, the values given have been established on standardized test specimens at room temperature. The figures should be regarded as guide values only and not as binding minimum values. Please note that, under certain conditions, the properties can be affected to a considerable extent by the design of the mold/die, the processing conditions and coloring.

Processing note

Under the recommended processing conditions small quantities of decomposition product may be given off during processing.To preclude any risk to the health and well-being of the machine operatives, tolerance limits for the work environment must be ensured by the provision of efficient exhaust ventilation and fresh air at the workplace in accordance with the Safety Data Sheet. In order to prevent the partial decomposition of the polymer and the generation of volatile decomposition products, the prescribed processing temperatures should not be substantially exceeded.