Bayblend ET1100 |
(PC+ABS) blend; 10 % mineral filled; extrusion grade; very high heat resistance; Vicat/B 120 = 142 °C; reduced coefficient of thermal dilatation; tensile modulus = 3300 MPa. |
|
|
|
Bayblend ET3032 FR |
Rubber modified PC blend; 10 % mineral filled; flame-retardant; extrusion grade; Vicat/B 120 temperature = 108 °C; good extrusion and vacuum-forming behaviour; UL 94 V-0 (0.75 mm) (Bayer internal test); halogen-free according to DIN VDE 0472,815; glow wire temperature (GWFI): 960 °C at 2.0 mm. |
|
|
|
Bayblend FR3000 |
(PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; easy-flow grade; Vicat/B 120 temperature = 97 °C; UL recognition 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm); no juicing; good light stability. |
|
|
|
Bayblend FR3000 HI |
(PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; general purpose; compared to FR3000 improved chemical resistance and stress cracking behavior; Vicat/B 120 temperature = 97 °C; UL recognition 94 V-0 at 1.5 mm. |
|
|
|
Bayblend FR3002 |
(PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; Vicat/B 120 temperature = 99 °C; UL recognition 94 V-0 (1.0 mm); antimony- chlorine- and bromine-free flame retardant; no juicing; glow wire test (GWFI): 960 °C (2.0 mm); for notebooks and thinwall applications. |
|
|
|
Bayblend FR3005 |
(PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; easy-flow grade; Vicat/B 120 temperature = 95 °C; UL recognition 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm); no juicing; good light stability. |
|
|
|
Bayblend FR3005 HF |
(PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; very easy-flow grade; Vicat/B 120 temperature = 96 °C; UL recognition 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant. |
|
|
|
Bayblend FR3006 |
(PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; high heat resistance; Vicat/B 120 = 110 °C; easy flow; UL recognition 94 V-1 at 1.5 mm and V-0 at 2.0 mm; antimony-, chlorine- and bromine-free flame retardant. |
|
|
|
Bayblend FR3008 |
(PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; improved chemical and hydrolysis resistance; HDT/A >= 85 °C; Vicat/B 120 temperature = 103 °C; UL recognition 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm); no juicing; good light stability. |
|
|
|
Bayblend FR3008 HR |
(PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; improved chemical and very good hydrolysis resistance; HDT/A >= 85 °C; Vicat/B 120 temperature = 103 °C; UL recognition 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm); no juicing; good light stability. |
|
|
|
Bayblend FR3010 |
(PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; increased heat resistance; Vicat/B 120 temperature = 110 °C; UL recognition 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm); improved chemical resistance and stress cracking behavior; successor to FR2010. |
|
|
|
Bayblend FR3010 IF |
(PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; increased heat resistance; Vicat/B 120 temperature = 108 °C; improved flammability; UL recognition 94 5VB (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm); improved flow compared to FR3010. |
|
|
|
Bayblend FR3011 |
(PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; good flow; high heat resistance; Vicat/B 120 temperature = 118 °C; UL recognition 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm); no juicing; good light stability. |
|
|
|
Bayblend FR3020 |
(PC+ABS) blend; 5 % mineral filled; flame retardant; for thin-wall applications; injection molding; Vicat/B 120 = 103 °C; HDT/A >= 85 °C; very good UL recognition in small wall thicknesses (V-0 at 0.75 mm); antimony-, chlorine- and bromine-free flame retardant. |
|
|
|
Bayblend FR3021 |
(PC+ABS) blend; 15 % mineral filled; flame retardant; injection molding grade; increased stiffness; tensile modulus = 4800 MPa; Vicat/B 120 temperature = 98 °C; UL recognition 94 V-0 (1.5 mm); antimony-, chlorine- and bromine-free flame retardant; glow wire test (GWFI): 960 °C (2.0 mm); no juicing. |
|
|
|
Bayblend FR3030 |
(PC+ABS) blend; unreinforced; flame-retardant; extrusion grade; Vicat/B 120 temperature = 115 °C; good extrusion and vacuum-forming behaviour; UL recognition 94 V-0 (1.5 mm); halogen-free according to DIN VDE 0472,815; glow wire temperature (GWFI): 960 °C at 1.0 mm. |
|
|
|
Bayblend FR3100 TV |
(PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; high heat resistance; Vicat/B 120 = 110 °C; improved impact strength and chemical resistance; UL recognition 94 V-1 at 1.5 mm and V-0 at 2.0 mm; antimony-, chlorine- and bromine-free flame retardant. |
|
|
|
Bayblend FR3110 TV |
(PC+ABS) blend; unreinforced; flame-retardant; injection molding grade; high heat resistance; Vicat/B 120 = 110 °C; easy flow; UL recognition 94 V-1 at 1.5 mm and V-0 at 2.0 mm; antimony-, chlorine- and bromine-free flame retardant. |
|
|
|
Bayblend FR410 MT |
Rubber modified PC blend; 10 % mineral filled; flame-retardant; injection molding grade; Vicat/B 120 = 108 °C; very good UL recognition in small wallthickness (V-0 at 0.75 mm); for railway interiors. The classifications according to the respective rail standards are communicated with email inquiry under pcs-info@bayermaterialscience.com. |
|
|
|
Bayblend KU2-1514 |
(PC+ABS) blend; unreinforced; flame-retardant; high heat resistant injection molding grade; ball indentation temperature >=125 °C; Vicat/B 120 temperature = 136 °C; UL recognition 94 V-0 at 1.5 mm; antimony-, chlorine- and bromine-free flame retardant; suitable for supporting life components. |
|
|
|
Bayblend KU2-1514 BBS073 |
(PC+ABS) blend; unreinforced; flame-retardant; high heat resistant injection molding grade; improved chemical resistance and stress cracking behavior compared to KU2-1514; ball indentation temperature >= 125 °C; Vicat/B 120 temperature = 136 °C; UL recognition 94 V-0 at 1.5 mm; antimony-, chlorine- and bromine-free flame retardant; suitable for supporting life components. |
|
|
|
Bayblend T45 PG |
(PC+ABS) blend; unreinforced; general purpose injection molding grade; Vicat/B 120 temperature = 112 °C; for electroplating applications. |
|
|
|
Bayblend T50 XF |
(PC+ABS) blend; unreinforced; injection molding grade; Vicat/B 120 = 115 °C; excellent flow; good low temperature impact strength. |
|
|
|
Bayblend T65 |
(PC+ABS) blend; unreinforced; general purpose injection molding grade; Vicat/B 120 temperature = 120 °C; good low temperature impact strength. |
|
|
|
Bayblend T65 HI |
(PC+ABS) blend; unreinforced; grade with improved low-temperature impact strength and chemical resistance for automotive parts; also suitable for extrusion/extrusion blow molding and electroplating applications; Vicat/B 120 temperature = 120 °C. |
|
|
|
Bayblend T65 XF |
(PC+ABS) blend; unreinforced; general purpose injection molding grade; Vicat/B 120 temperature = 120 °C; improved flowability compared to T65. |
|
|
|
Bayblend T80 XG |
(PC+ABS) blend; unreinforced; injection molding grade; Vicat/B 120 temperature = 127 °C; excellent flow; optimized surface quality for metallization (steam treatment). |
|
|
|
Bayblend T85 |
(PC+ABS) blend; unreinforced; general purpose injection molding grade; Vicat/B 120 temperature = 131°C; high impact and notched impact strength. |
|
|
|
Bayblend T85 XF |
(PC+ABS) blend; unreinforced; injection molding grade; Vicat/B 120 temperature = 130 °C; better flow than T85. |
|
|
|
Bayblend T88 GF-10 |
Rubber modified (PC+SAN) blend; 10 % glass fiber filled; injection molding grade; optimized heat ageing- and UV-stability; very good flow; tensile modulus = 5100 MPa; Vicat/B 120 = 134 °C. |
|
|
|
Bayblend T88 GF-20 |
Rubber modified (PC+SAN) blend; 20 % glass fiber filled; injection molding grade; optimized heat ageing- and UV-stability; very good flow; tensile modulus = 7500 MPa; Vicat/B 120 = 130 °C. |
|
|
|
Bayblend T88 GF-30 |
Rubber modified (PC+SAN) blend; 31 % glass fiber filled; injection molding grade; optimized heat ageing- and UV-stability; very good flow; tensile modulus = 10000 MPa; Vicat/B 120 = 134 °C. |
|
|
|
Bayblend T90 |
(PC+ABS) blend; unreinforced; injection molding grade; Vicat/B 120 temperature = 127 °C; excellent flow., For thinwall technology applications. |
|
|
|
Bayblend T90 HT |
(PC+ABS) blend; unreinforced; injection molding grade; high heat resistance; Vicat/B 120 = 135 °C; ball indentation temperature >= 125 °C; easy flow; suitable for supporting life components. |
|
|
|
Bayblend T90 MF-20 |
Rubber modified (PC+SAN) blend; 20 % mineral filled; injection molding grade; very good flow; reduced coefficient of thermal dilatation; tensile modulus = 4900 MPa; Vicat/B 120 = 130 °C. |
|
|
|
Bayblend T95 MF |
(PC+ABS) blend; 9 % mineral filled; injection molding grade; very high heat resistance; Vicat/B 120 = 142 °C; reduced coefficient of linear thermal expansion; tensile modulus = 3350 MPa. |
|
|
|
Bayblend W85 XF |
(PC+ASA) blend; unreinforced; injection molding grade with improved weather resistance; optimized heat ageing stability; high heat resistance; Vicat/B 120 = 132 °C. |
|